Adhesive-grade Fluorosilicone FVMQ Compound with High Strength, Good Resilience, and Metal Adhesion
Product Details
High Strength FVMQ Compound
,Good Resilience Fluorosilicone Compound
,Metal Adhesion Adhesive-grade Sealant
- Excellent mechanical performance
- High strength and resilience
- Superior adhesion to metal surfaces
- Metal-coated rubber products
| Test Item | Standard | Value |
|---|---|---|
| Hardness | shoreA | 60 |
| Tensile Strength | MPa | 9 |
| Elongation at Break | % | 300 |
| Heat Aging (200℃ *72h) | Strength ChangeA | 3 |
| Strength Change | - | -20 |
| Strength Change % | - | -20 |
| Fuel C (25℃ *72h) | Volume Change % | 20 |
| Type B Compression Set | 177°C*72h | 10 |
| Density | g/cm³ | 1.45 |
Transparent Waterproof Tear-resistant PVC Mesh Tarpaulin and PVC Laminated Mesh Fabric for Agriculture Construction Factory Enclosures
High-transparency PVC laminated mesh tarpaulin: polyester mesh core with clear PVC films for waterproof, tear-resistant, durable performance. Flexible, easy to cut, heat-seal and weld. Ideal for greenhouse curtains, construction hoardings, factory partitions and protective covers. Custom thickness and width available.
Rubber fender with UHMW-PE plate for yachts offering medium energy absorption and high abrasion resistance
Rubber fenders with UHMW-PE plates offer medium energy absorption, high reaction force, and excellent abrasion resistance. Available for bow and side yacht applications with durable construction.
Elastic Self-adhesive Thermal Conductive Pad with Thermal Conductivity 1.0 W/m-K to 9.0 W/m-K for Heat Dissipation
Self-adhesive thermal pads with 1.0-9.0 W/m-K conductivity. Excellent elasticity fills air gaps, reduces thermal resistance, and improves heat dissipation in 5G, automotive, and industrial applications. No backing adhesive required.
High-temperature Resistant and Oil-resistant FKM Fluororubber O-rings and Seals for Automotive Engine with Custom-shaped Parts
FKM Fluororubber O-rings and seals offer exceptional high-temperature and oil resistance for automotive engines. With 66% fluorine content, superior tensile strength (12 MPa), and easy molding properties, they ensure reliable performance and durability in demanding applications.